Overture Matte PLA Dual Colors 3D Printer Filament 1.75mm

INTRODUCTION

• 【High-Grade Matte PLA】This newly launched filaments can output prints with shine-free color and frosted texture, which make it perfect for creation needing low-key, rich and enigmatic appearance;Grid layout on the surface for easy resizing
• 【Easy to Print & More Humanized Design】Easy to print just like normal PLA, more likely to get quality prints with sharp details. Excellent threshold overhang angle. Raft and support are very easy to remove; Reel with length/ weight gauge and viewing hole so that you can easily figure out the remaining filaments; more filaments clip holes for fixing purpose on the reel; Larger spool inner diameter design makes feeding smoother
• 【Odorless & No Bubble】Developed based on Natural PLA, this Matte PLA filaments deliver excellent printing quality with no odor and low warpage during printing; Complete drying for 24 hours before vacuum packaging to effectively protect the filament from moisture, no stringing and bubble-free
• 【Dimensional Accuracy & Consistency】advanced CCD diameter measuring and self-adaptive control system in the manufacturing guarantee these PLA filaments of 1.75 mm diameter, Accuracy +/- 0.03 mm; 1 kg spool (2.2lbs)
• 【Cost-effective and Wide Compatibility】With over 9 years' 3D filaments R & D experience, thousands tons of filaments output every month, Overture is capable of manufacturing all kinds of filaments in large scale with premium quality, which contribute to Overture filament cost-effective and reliable for most common 3D printers, such as MK3, Ender 3, Monoprice FlashForge and more

Buy with Confidence, 100% Satisfaction Guarantee. E-mail us if you have any issues or questions, we will make every effort to provide you with immediate help until you are satisfied.

SPECIFICATIONS

• Density：1.32 ±0.1 (g/cm3 at 21.5˚C)
• Tensile strength (X-Y) ：20.90 ± 1.95 (MPa)
• Tensile strength (Z)：18.01 ±0.29 (%)
• Elongation at break (X-Y)：34.45 ± 8.06 (%)
• Bending modulus ：2694 ± 541.18 (MPa)
• Bending strength ：39.6 ± 1.1(MPa)
• Charpy impact strength：5.66 ± 0.44 (kJ/m2)
• Young’s modulus (X-Y) ：1882 ± 141.12 (MPa)

• Recommended Extrusion/Nozzle Temp: 190°C - 220°C (374℉~ 428℉)
• Heated Bed Temp: 50°C - 70°C (122℉ ~ 158℉)
• Dimensional Accuracy 99% Probability +/- 0.03mm
• Dimensional Accuracy 98% Probability +/- 0.02mm
• Printing Speed: 30~70 mm/s (1800mm~4200 mm/min)
• Filaments Net Weight: 1 kg (2.2 lbs)